Leaching of lepidolite and recovery of lithium hydroxide from purified alkaline pressure leach liquor by phosphate precipitation and lime addition

James Mulwanda, Gamini Senanayake, Hans Oskierski, Mohammednoor Altarawneh, Bogdan Z. Dlugogorski

Research output: Contribution to journalArticlepeer-review

14 Citations (Scopus)

Abstract

This study investigated the pressure leaching of lithium and other valuable metals from lepidolite using NaOH and Ca(OH)2. The findings showed that NaOH concentration, temperature, and stirring rate are the most significant process parameters. The addition of Ca(OH)2 facilitates the leaching of lithium and minimizes the concentration of silicate and fluoride in the leach liquor by forming solid phases identified as Ca3Al2Si3O12, CaF2 and NaCaHSiO4, with a loss of about 7% NaOH. The leaching efficiencies after 2 h were 94% Li, 98% K, 96% Rb, and 90% Cs under the most suitable conditions (250 °C, 320 g/L NaOH, liquid-to-solid ratio of 10, 300 rpm stirring speed, lime addition of 0.3 g/g). Precipitation of lithium as Li3PO4 by adding phosphoric acid and subsequent conversion of Li3PO4 to LiOH using Ca(OH)2 recovered 83% of lithium as LiOH allowing recycling the rest along with residual remnant NaOH for leaching.

Original languageEnglish
Article number105538
JournalHydrometallurgy
Volume201
DOIs
Publication statusPublished - May 2021

Keywords

  • Alkaline
  • Caesium
  • Leaching
  • Lepidolite
  • Lithium
  • Phosphate/hydroxide precipitation
  • Potassium
  • Pressure
  • Rubidium

ASJC Scopus subject areas

  • Metals and Alloys
  • Industrial and Manufacturing Engineering
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Leaching of lepidolite and recovery of lithium hydroxide from purified alkaline pressure leach liquor by phosphate precipitation and lime addition'. Together they form a unique fingerprint.

Cite this