High-temperature strength and storage modulus in unidirectional hybrid composites

E. J. Bosze, A. Alawar, O. Bertschger, Yun I. Tsai, S. R. Nutt

Research output: Contribution to journalArticlepeer-review

48 Citations (Scopus)

Abstract

The mechanical properties of pultruded rods of unidirectional hybrid glass/carbon-epoxy composites were evaluated with respect to retention of high-temperature properties up to 250 °C. Two prototype matrices were produced using developmental epoxy formulations with glass transition temperatures (Tg) of 176 and 202 °C, respectively. The two prototype composites showed diminished tensile strength at high temperatures, but with different temperature thresholds. The high-Tg composite retained full strength to 170 °C, while the lower-Tg composite retained full strength to 80 °C. Matrix softening and loss of fiber-matrix adhesion was a major factor affecting the strength reduction observed at high temperatures. The storage modulus, measured by dynamic mechanical analysis (DMA), showed temperature dependence nearly identical to the tensile strength for both composites. The correlation between storage modulus and tensile strength was analyzed in terms of the effect of temperature on the shear modulus of the matrices. The storage modulus behavior is presented as a basis for projecting the strength-temperature dependence of unidirectional composites.

Original languageEnglish
Pages (from-to)1963-1969
Number of pages7
JournalComposites Science and Technology
Volume66
Issue number13
DOIs
Publication statusPublished - Oct 2006

Keywords

  • A. Carbon fibers
  • A. Glass fibers
  • B. Fiber/matrix bond
  • B. Thermomechanical properties
  • E. Pultrusion

ASJC Scopus subject areas

  • Ceramics and Composites
  • Engineering(all)

Fingerprint

Dive into the research topics of 'High-temperature strength and storage modulus in unidirectional hybrid composites'. Together they form a unique fingerprint.

Cite this