High-pressure electrical resistivity and Mössbauer spectroscopic studies on narrow band Co 0.8Fe 0.2S 2 nanoparticles up to 8 GPa

Usha Chandra, I. Zuburtikudis, G. Parthasarathy, B. Sreedhar

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)

Abstract

Pyrite-structured Co0.8Fe0.2S2 colloid nanoparticles, synthesized using solution method with particle distribution around 3-4 nm determined by transmission electron microscope, were studied under high pressure up to 8 GPa using 57Fe Mössbauer spectroscopy and electrical resistivity techniques. Drastic decrease in TC by magnetic measurements indicated nanosize of the particle. Higher quadrupole splitting (QS) at ambient condition was due to large lattice strain and electric field gradient generated by higher surface to volume ratio of these nanosized particles. Under pressure, Mössbauer parameters-isomer shift and QS-showed an expected trend up to ∼5.6 GPa. Above 6.4 GPa, the QS remained constant up to 8 GPa with decreased value. Even after decompression, the high-pressure phase is retained. The variation of pressure coefficient of electrical resistivity from-0.021/GPa to-0.151/GPa across 6.8 GPa suggested a second-order phase transition. The coincidence of observed value with that of the bulk suggested that the particle size does not impart much influence on transition pressure. This is the first report on nanoparticles of Co0.8Fe 0.2S2 under pressure.

Original languageEnglish
Pages (from-to)477-490
Number of pages14
JournalPhase Transitions
Volume87
Issue number5
DOIs
Publication statusPublished - May 4 2014

Keywords

  • M€ossbauer spectroscopy
  • diamond anvil cell
  • electrical resistivity
  • high pressure
  • nanoparticles
  • pyrite

ASJC Scopus subject areas

  • Instrumentation
  • Materials Science(all)

Fingerprint

Dive into the research topics of 'High-pressure electrical resistivity and Mössbauer spectroscopic studies on narrow band Co 0.8Fe 0.2S 2 nanoparticles up to 8 GPa'. Together they form a unique fingerprint.

Cite this