Durability and fatigue of basalt fiber-reinforced polymer bars gripped with steel wedge anchors

Ahmed El Refai

Research output: Contribution to journalArticlepeer-review

46 Citations (Scopus)

Abstract

This paper presents the test results of a durability study on a novel basalt fiber-reinforced polymer (BFRP) bar-anchor system. The BFRP bars were exposed to saline and alkaline solutions for 10 weeks before being anchored and tested under static and fatigue loading. Unconditioned basalt, glass, and carbon specimens were also tested and served as controls. Regardless of the fiber material, all the bar-anchor systems withstood their ultimate tensile loading with no sign of slippage or premature failure in the anchor zones. Conditioning of the BFRP bars in saline and alkaline solutions resulted in 7 and 9% decreases, respectively, in the systems' tensile capacity. A decrease of 11% in the modulus of the alkali-conditioned BFRP specimens was also observed. The fatigue test results showed that the fatigue life of the bar-anchor system was primarily affected by the applied stress range. In addition, continuous immersion of the BFRP bar in the alkaline solution increased its tendency to fracture prematurely in the anchor zone. The fatigue limit of the BFRP bar-anchor system was determined to be 4% of its ultimate capacity, compared with 3 and 10% for the glass and carbon systems, respectively.

Original languageEnglish
Article number04013006
JournalJournal of Composites for Construction
Volume17
Issue number6
DOIs
Publication statusPublished - Dec 2013

Keywords

  • Aging
  • Anchors
  • Basalt
  • Durability
  • Fatigue
  • Fiber reinforced polymer
  • Glass fibers
  • Prestressing
  • Tensile loads

ASJC Scopus subject areas

  • Ceramics and Composites
  • Civil and Structural Engineering
  • Building and Construction
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Durability and fatigue of basalt fiber-reinforced polymer bars gripped with steel wedge anchors'. Together they form a unique fingerprint.

Cite this