Development and characterization of fly ash-slag blended geopolymer mortar and lightweight concrete

Najif Ismail, Hilal El-Hassan

Research output: Contribution to journalArticlepeer-review

42 Citations (Scopus)

Abstract

A synopsis of an experimental program on the development of a sustainable fly ash-slag blended geopolymer mortar (GPM) and lightweight geopolymer concrete (LGPC) is presented. Geopolymer mortar mixes were prepared incorporating industrial by-products and sustainable desert dune sand to study the effect of different mixing variables, including binding materials, curing temperature, and alkaline activator solution composition and content, on the rheological and mechanical performance. Optimum mix designs were then formulated into producing LGPC samples with different binding materials and curing temperature. Lightweight geopolymer concrete specimens exhibited a brittle behavior with a weakened structure due to low-strength lightweight aggregates. Lightweight geopolymer concrete made with dune sand and a fly ash to slag ratio of 3:1 resulted in the highest compressive strength when cured for 24 h at 60°C. Microstructure characterization of LGPC specimens was also conducted. Scanning electron microscopy and differential scanning calorimetry showed the coexistence of an aluminosilicate hydrate geopolymer gel and aluminum-modified C-S-H gel as the main polymerization reaction products in an amorphous geopolymeric microstructure.

Original languageEnglish
Article number04018029
JournalJournal of Materials in Civil Engineering
Volume30
Issue number4
DOIs
Publication statusPublished - Apr 1 2018

Keywords

  • Dune sand
  • Geopolymer
  • Lightweight
  • Mechanical
  • Microstructure
  • Rheological

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Building and Construction
  • Materials Science(all)
  • Mechanics of Materials

Fingerprint

Dive into the research topics of 'Development and characterization of fly ash-slag blended geopolymer mortar and lightweight concrete'. Together they form a unique fingerprint.

Cite this